壳聚糖与丙烯酸接枝共聚反应的研究,页数 34 字数 15907附开题报告摘要：本文研究了壳聚糖和丙烯酸单体在不同反应条件下的接枝共聚反应，并通过正交试验设计法找出一组最优反应工艺条件。并讨论了温度、时间、单体质量比及引发剂浓度对接枝共聚反应的影响。本文还利用红外光谱分析法对壳聚糖的结构进行了表征。关键词：壳聚糖,接枝共聚...
内容介绍
此文档由会员 张阳阳 发布
壳聚糖与丙烯酸接枝共聚反应的研究
页数 34 字数 15907 附开题报告
摘要：
本文研究了壳聚糖和丙烯酸单体在不同反应条件下的接枝共聚反应，并通过正交试验设计法找出一组最优反应工艺条件。并讨论了温度、时间、单体质量比及引发剂浓度对接枝共聚反应的影响。本文还利用红外光谱分析法对壳聚糖的结构进行了表征。
关键词：壳聚糖,接枝共聚反应,丙烯酸,正交试验设计法
Abstract：
This article investigateed the graft copolymerization of acrylic acid onto chitosan under different reaction conditions ,and found the best technical condition of graft copolymerization by using the orthogonality experimental design method. In addition,the different effect of reaction temperature ，time,monomer quality ratio and initiator concentration on grafting percentage and grafting efficiency was also discussed. At last, the dissolution capability of the graft copolymer was tested in different impregnant. The graft copolymer was also characterized by IR.
Keywards: chitosan; graft copolymerization; acrylic acid; orthogonality
experimental design method
目录
关键词：壳聚糖；接枝共聚反应；丙烯酸；正交试验设计法 0
The Research of The Graft Copolymerization of 0
Acrylic Acid onto Chitosan 0
引言 1
1．壳聚糖的简介和发展概况壳聚糖 1
1．1壳聚糖简介[1-6] 1
1．1．1壳聚糖的制备方法[7] 2
1．1．2壳聚糖的化学性质[8-12] 2
1．1．3壳聚糖的生物学性质 4
1．2壳聚糖的发展概况及应用[7] 5
1．2．1壳聚糖的发展概况 5
1．2．2壳聚糖的应用 5
2．接枝共聚反应[17-18] 6
3．正交试验设计方法[19] 7
4．实验部分 8
4．1原料及试剂 8
4．2实验仪器及器皿 8
4．3本实验的反应机理 8
4．4聚合反应实施方法的选择[20-21] 9
4．5引发剂的选择 9
4．6实验过程 10
4．6．1前期工作准备 10
4．6．2壳聚糖接枝丙烯酸接枝共聚物的制备过程 10
4．6．3壳聚糖与丙烯酸接枝共聚物的分离及提纯[22-24] 10
4．6．4各个反应条件对接枝共聚反应的影响 10
5．结果和分析 12
5．1红外光谱分析 12
对壳聚糖和壳聚糖接枝丙烯酸共聚物进行红外光谱分析，得到图5.1、图5.2分别为壳聚糖的红外光谱图，壳聚糖接枝丙烯酸共聚物的红外光谱图，如图所示： 12
5．2接枝率和接枝效率的计算 13
5．3各个反应条件对接枝共聚反应的影响的讨论 15
5．3．1反应时间对接枝共聚反应的影响 15
以表4.1中的时间为横坐标，接枝率和接枝效率分别为纵坐标绘制反应时间对接枝率和接枝效率的关系曲线如图5.1所示： 15
5．3．2反应温度对接枝共聚反应的影响 15
5．3．3单体质量比对接枝共聚反应的影响 16
5．3．4引发剂浓度对接枝共聚反应的影响 17
6．结论 17
参考文献 18
致 谢 19
附录 20
开题报告 20
中期报告 22
英文资料翻译 23
英文原文 32
参考文献
[1]Q.Li:J.Bioactive and Compatible Polymers.1992:370～397
[2]陶薇薇,李兆龙.化工物质.1990,(3):24～29
[3]P.Roy-Chowdhury.et al.J.Appl Polym.Sci.1984,29:153
[4]王伟,徐德.化学学报.1994,52(3):243～247
[5]许崇泉等,化学与粘合.1990,(2):63～65
[6]R.Muzzarelli.Chitin in Nature and Technology IN:proceedings of the Third
页数 34 字数 15907 附开题报告
摘要：
本文研究了壳聚糖和丙烯酸单体在不同反应条件下的接枝共聚反应，并通过正交试验设计法找出一组最优反应工艺条件。并讨论了温度、时间、单体质量比及引发剂浓度对接枝共聚反应的影响。本文还利用红外光谱分析法对壳聚糖的结构进行了表征。
关键词：壳聚糖,接枝共聚反应,丙烯酸,正交试验设计法
Abstract：
This article investigateed the graft copolymerization of acrylic acid onto chitosan under different reaction conditions ,and found the best technical condition of graft copolymerization by using the orthogonality experimental design method. In addition,the different effect of reaction temperature ，time,monomer quality ratio and initiator concentration on grafting percentage and grafting efficiency was also discussed. At last, the dissolution capability of the graft copolymer was tested in different impregnant. The graft copolymer was also characterized by IR.
Keywards: chitosan; graft copolymerization; acrylic acid; orthogonality
experimental design method
目录
关键词：壳聚糖；接枝共聚反应；丙烯酸；正交试验设计法 0
The Research of The Graft Copolymerization of 0
Acrylic Acid onto Chitosan 0
引言 1
1．壳聚糖的简介和发展概况壳聚糖 1
1．1壳聚糖简介[1-6] 1
1．1．1壳聚糖的制备方法[7] 2
1．1．2壳聚糖的化学性质[8-12] 2
1．1．3壳聚糖的生物学性质 4
1．2壳聚糖的发展概况及应用[7] 5
1．2．1壳聚糖的发展概况 5
1．2．2壳聚糖的应用 5
2．接枝共聚反应[17-18] 6
3．正交试验设计方法[19] 7
4．实验部分 8
4．1原料及试剂 8
4．2实验仪器及器皿 8
4．3本实验的反应机理 8
4．4聚合反应实施方法的选择[20-21] 9
4．5引发剂的选择 9
4．6实验过程 10
4．6．1前期工作准备 10
4．6．2壳聚糖接枝丙烯酸接枝共聚物的制备过程 10
4．6．3壳聚糖与丙烯酸接枝共聚物的分离及提纯[22-24] 10
4．6．4各个反应条件对接枝共聚反应的影响 10
5．结果和分析 12
5．1红外光谱分析 12
对壳聚糖和壳聚糖接枝丙烯酸共聚物进行红外光谱分析，得到图5.1、图5.2分别为壳聚糖的红外光谱图，壳聚糖接枝丙烯酸共聚物的红外光谱图，如图所示： 12
5．2接枝率和接枝效率的计算 13
5．3各个反应条件对接枝共聚反应的影响的讨论 15
5．3．1反应时间对接枝共聚反应的影响 15
以表4.1中的时间为横坐标，接枝率和接枝效率分别为纵坐标绘制反应时间对接枝率和接枝效率的关系曲线如图5.1所示： 15
5．3．2反应温度对接枝共聚反应的影响 15
5．3．3单体质量比对接枝共聚反应的影响 16
5．3．4引发剂浓度对接枝共聚反应的影响 17
6．结论 17
参考文献 18
致 谢 19
附录 20
开题报告 20
中期报告 22
英文资料翻译 23
英文原文 32
参考文献
[1]Q.Li:J.Bioactive and Compatible Polymers.1992:370～397
[2]陶薇薇,李兆龙.化工物质.1990,(3):24～29
[3]P.Roy-Chowdhury.et al.J.Appl Polym.Sci.1984,29:153
[4]王伟,徐德.化学学报.1994,52(3):243～247
[5]许崇泉等,化学与粘合.1990,(2):63～65
[6]R.Muzzarelli.Chitin in Nature and Technology IN:proceedings of the Third